Modified PA66
Classification:
Product Introduction
Product Details
Modified PA66
| Toughened PA66 | ||
| Serial Number | Type | Grade |
| 1 | Natural toughened PA66 (heat and aging resistant) | A531 |
| 2 | Black toughened PA66 (heat and aging resistant) | A531B02 |
| Glass fiber reinforced PA66 | ||
| 1 | Natural PA66+GF10 | A52G10 |
| 2 | Natural PA66+GF20 | A52G20 |
| 3 | Natural PA66+GF30 | A52G30 |
| 4 | Natural PA66+GF50 | A52G50NC |
| 5 | Black reinforced hydrolysis-resistant PA66 | A52G30BAH |
| Glass fiber reinforced toughened PA66 | ||
| 2 | Natural toughened PA66+GF15 | A51G15 |
| 1 | Black toughened PA66+GF30 (heat and aging resistant) | A51G30B01 |
| 1 | Natural toughened PA66+GF30 | A51G30NC010 |
| 3 | Natural toughened PA66+GF30 | A51G30NC015 |
| 4 | Natural toughened PA66+GF30 | A51G30NC011 |
| 5 | Natural toughened PA66+GF33 | A51G3311 |
| Flame retardant PA66 | ||
| 1 | Natural nitrogen-based V0 flame retardant PA66 | A52NHNC08 |
| 2 | Black red phosphorus V0 flame retardant PA66 | A52NHB05 |
| Reinforced flame retardant PA66 | ||
| 1 | Black red phosphorus V0 flame retardant reinforced PA66 | A52G25NHB03 |
| 2 | Natural phosphorus-nitrogen based V0 flame retardant reinforced PA66 | A52G30NH |
| 3 | Gray bromine-based V0 flame retardant reinforced PA66 | A52G25NGY16 |
| Other modified PA66 | ||
| 1 | Orange PA66 | A52O15 |
| 2 | Black heat and aging resistant PA66 | A52B01HR |
Toughened PA66
Product introduction: Toughened modified PA66, mainly used in automotive wire harness cable ties, buckles, etc., widely used in automobiles, power tools, sports equipment, industrial parts and other fields with demanding comprehensive mechanical properties (especially impact resistance).
Product details: Toughened modified PA66, injection molding grade, with excellent high impact resistance, low temperature resistance and long-term heat aging resistance.
| Main Performance Items | Unit | Test Standard | Natural toughened PA66 (heat and aging resistant) A531 |
Black toughened PA66 (heat and aging resistant) A531B02 |
| Density | g/cm3 | ISO 1183 | 1.119 | 1.212 |
| Ash content | % | ISO 3451 | / | / |
| Tensile strength | MPa | ISO 527 | 67 | 29 |
| Elongation at break | % | ISO 527 | 24 | 36 |
| Flexural strength | MPa | ISO 178 | 94 | 82 |
| Flexural modulus | MPa | ISO 178 | 2559 | 2242 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 18.4 | 19.4 |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 17.1 | 12.8 |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 346 | 356 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 90 | 94 |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 40.3 | 41.3 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 69 | 70 |
Glass fiber reinforced PA66
Product introduction: Glass fiber reinforced modified PA66, mainly used in automotive connectors and other automotive parts. With its excellent comprehensive performance, it has become one of the preferred materials to replace metal, especially playing an irreplaceable role in the automotive, electronic and electrical, and industrial machinery fields.
Product details: Glass fiber reinforced PA66, injection molding grade, with excellent mechanical properties and heat resistance, good dimensional stability and molding processability.
| Main Performance Items | Unit | Test Standard | Natural PA66+GF10 A52G10 |
Natural PA66+GF20 A52G20 |
Natural PA66+GF30 A52G30 |
Natural PA66+GF50 A52G50NC |
Black reinforced hydrolysis-resistant PA66 A52G30BAH |
| Density | g/cm3 | ISO 1183 | 1.191 | 1.28 | 1.362 | 1.555 | 1.381 |
| Ash content | % | ISO 3451 | 10 | 20 | 30 | 50 | 32 |
| Tensile strength | MPa | ISO 527 | 112 | 149 | 196 | 218 | 199 |
| Elongation at break | % | ISO 527 | 7 | 6 | 7 | 7 | 7 |
| Flexural strength | MPa | ISO 178 | 163 | 222 | 289 | 331 | 294 |
| Flexural modulus | MPa | ISO 178 | 4140 | 6280 | 9059 | 13108 | 9550 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 7.8 | 9.7 | 15.8 | 22.5 | 14.3 |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 7.6 | 8.9 | 13.2 | 19.9 | 11.2 |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 52 | 69 | 98 | 129 | 96 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 36 | 58 | 87 | 116 | 65 |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 22.3 | 23.3 | 10.3 | 3.1 | 10 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 209 | 241 | 251 | 243 | 250 |
Glass fiber reinforced toughened PA66
Product introduction: Glass fiber reinforced toughened modified PA66, mainly used in automotive shock absorbers, automotive connectors, and high-speed rail fastening parts, replacing metal in high-temperature, high-load, and strong impact environments, and is a core material in high-speed rail, automotive, electronics, and machinery fields.
Product details: Glass fiber reinforced toughened PA66, injection molding grade, with excellent mechanical properties and heat resistance, good impact resistance, dimensional stability, and molding processability.
| Main Performance Items | Unit | Test Standard | Natural PA66+GF15 A51G15 |
Black toughened PA66+GF30 (Heat and aging resistant) A51G30B01 |
Toughened PA66+GF30 A51G30NC010 |
Toughened PA66+GF30 A51G30NC011 |
Toughened PA66+GF30 A51G30NC015 |
Toughened PA66+GF33 A51G3311 |
| Density | g/cm3 | ISO 1183 | 1.233 | 1.36 | 1.327 | 1.377 | 1.306 | 1.344 |
| Ash content | % | ISO 3451 | 15 | 30 | 30 | 34 | 30 | 33 |
| Tensile strength | MPa | ISO 527 | 129 | 163 | 152 | 178 | 147 | 161 |
| Elongation at break | % | ISO 527 | 7 | 6.4 | 7 | 8 | 8 | 7 |
| Flexural strength | MPa | ISO 178 | 187 | 239 | 220 | 267 | 218 | 235 |
| Flexural modulus | MPa | ISO 178 | 5083 | 8110 | 6860 | 9134 | 7039 | 7711 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 12 | 20.4 | 22.3 | 25 | 30.4 | / |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 7.8 | 15.3 | 16.2 | 18 | 23.8 | / |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 91 | 92 | 117 | 108 | 104 | 102 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 52 | 81 | 115 | 111 | 104 | / |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 24.9 | 3.6 | 8.1 | 6.7 | 3.1 | 3.1 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 233 | 236 | 237 | 249 | 228 | 239 |
| Melting point | ℃ | ISO 11357 | / | / | / | 267.9 | / | 274.2 |
| Volume resistivity | Ω | IEC 60093 | / | / | 1.342×1015 (dry state) | 3.241×1015 (dry state) | / | 2.141×1015 (dry state) |
| 1.187×1015 (wet state) | 4.909×1011 (wet state) | 1.016×1011 (wet state) |
Flame retardant PA66
Product introduction: Flame-retardant modified PA66, mainly used in electronic connectors, household appliances, energy storage and many other safety-sensitive industries.
Product details: Flame-retardant PA66, nitrogen-based and phosphorus-based, injection molding grade, with excellent flame retardancy, superior comprehensive mechanical properties, good heat resistance and electrical insulation, and molding processability.
| Main Performance Items | Unit | Test Standard | Natural color nitrogen-based V0 flame retardant A52NHNC08 |
Black red phosphorus V0 flame retardant A52NHB05 |
| Density | g/cm3 | ISO 1183 | 1.171 | 1.188 |
| Ash content | % | ISO 3451 | / | / |
| Tensile strength | MPa | ISO 527 | 116 | 57 |
| Elongation at break | % | ISO 527 | 11 | 18 |
| Flexural strength | MPa | ISO 178 | 105 | 88 |
| Flexural modulus | MPa | ISO 178 | 2963 | 2696 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 9.4 | 7.8 |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 8.8 | 7.3 |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 36 | 86 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 45 | 79 |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 85.5 | 16.3 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 73 | 74 |
| Flame retardant performance | 1.6mm | UL94 | V-0 | - |
| 3.2mm | V-0 | V-0 |
Reinforced flame retardant PA66
Product introduction: Glass fiber reinforced flame-retardant modified PA66, mainly used in electronic appliances, new energy vehicles and industrial parts requiring heat resistance and flame retardancy.
Product details: Glass fiber reinforced flame-retardant PA66, phosphorus-based, phosphorus-nitrogen-based and bromine-based, injection molding grade, with excellent flame retardancy, high strength and high rigidity.
| Main Performance Items | Unit | Test Standard | Black red phosphorus V0 flame retardant enhanced 25 A52G25NHB03 |
Natural color phosphorus-nitrogen-based V0 flame retardant enhanced 30 A52G30NH |
Gray bromine-based V0 flame retardant enhanced 25 A52G25NGY16 |
| Density | g/cm3 | ISO 1183 | 1.417 | 1.417 | 1.547 |
| Ash content | % | ISO 3451 | 32 | 33 | 29 |
| Tensile strength | MPa | ISO 527 | 145 | 136 | 137 |
| Elongation at break | % | ISO 527 | 5 | 2 | 6 |
| Flexural strength | MPa | ISO 178 | 207 | 200 | 204 |
| Flexural modulus | MPa | ISO 178 | 8761 | 8769 | 8501 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 8.8 | 9.4 | 11.4 |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 7.9 | 9.9 | 9.2 |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 59 | 56 | 72 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 47 | 51 | 57 |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 7.8 | 25.4 | 31.5 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 229 | 216 | 225 |
| Flame retardant performance | 1.6mm | UL94 | V-0 | V-0 | V-0 |
| 3.2mm | - | V-0 | V-0 |
Other modified PA66
Product introduction: Color-modified PA66 and heat-aging-resistant modified PA66, mainly used in new energy vehicle connectors and high-speed rail baffle seats.
Product details: Color-matched PA66 and heat-aging-resistant PA66, injection molding grade, with high fluidity and long-term heat aging resistance.
| Main Performance Items | Unit | Test Standard | Orange PA66 A52O15 |
Black heat and aging resistant PA66 A52B01HR |
| Density | g/cm3 | ISO 1183 | 1.145 | 1.143 |
| Ash content | % | ISO 3451 | / | / |
| Tensile strength | MPa | ISO 527 | 82 | 84 |
| Elongation at break | % | ISO 527 | 7 | 17 |
| Flexural strength | MPa | ISO 178 | 110 | 116 |
| Flexural modulus | MPa | ISO 178 | 2963 | 3065 |
| Notched Izod impact strength (23℃) | KJ/m2 | ISO 180 | 7.5 | 9.5 |
| Notched Izod impact strength (-40℃) | KJ/m2 | ISO 180 | 8.8 | 10.7 |
| Charpy unnotched impact strength (23℃) | KJ/m2 | ISO 179 | 249 | 376 |
| Charpy unnotched impact strength (-40℃) | KJ/m2 | ISO 179 | 87 | 125 |
| Melt flow index (275℃/2.16kg) | g/10min | ISO 1133 | 60.8 | 10.7 |
| Heat deflection temperature (1.8 MPa) | ℃ | ISO 75 | 76 | 84 |
Key words:
Online Message
Leave a message immediately and get the product quotation free of charge. We will arrange the specialist to contact you as soon as possible.